粉末冶金技术论文
粉末冶金技术
摘要：粉末冶金是制取金属或用金属粉末（或金属粉末与非金属粉末的混合物）作为原料，经过成
形和烧结，制造金属材料、复合以及各种类型制品的工艺技术。粉末冶金法与生产陶瓷有相似的地方，因此，一系列粉末冶金新技术也可用于陶瓷材料的制备。粉末冶金材料是指用几种金属粉末或金属与非金属粉末作原料，通过配料、压制成形、烧结等工艺过程而制成的材料。这种工艺过程成为粉末冶金法，是一种不同于熔炼和铸造的方法。其生产过程与陶瓷制品相类似，所以又称金属陶瓷法。粉末冶金法不仅是制取具有某些特殊性能材料的方法，也是一种无切削或少切削的加工方法。它具有生产率高、材料利用率高、节省机床和生产占地面积等优点。但金属粉末和模具费用高，制品大小和形状受到一定限制，制品的韧性较差。粉末冶金法常用于制作硬质合金、减摩材料、结构材料、摩擦材料、难熔金属材料、过滤材料、金属陶瓷、无偏析高速工具钢、磁性材料、耐热材料等。
关键词：粉末冶金、基本工序、应用、发展方向、问题及机遇
Powder metallurgy technology
(11 grade material class two)
Abstract:Powder metallurgy is used for preparing metal or metal powder (or metal powder
and metal powder mixture) as raw material, after forming and sintering, manufacture of metal materials, composite and various types of products technology.Powder metallurgy method and the production of ceramic have similar place, therefore, a series of new powder metallurgy technologies can also be used for preparing ceramic material. Powder metallurgy materials refers to the use of several kinds of metal powder or metal and non metal powder as raw material, through mixing, pressing, sintering process and made of materials.The process to become powder metallurgy method, is different from the melting and casting method.Its production process and ceramic products are similar, so called ceramic metal.Powder metallurgy method not only has some special properties of material preparation method, is also a kind of without cutting or less cutting processing method. It has high productivity, high material utilization rate, saving machine tools and production area etc..But the metal powder and high mold cost, product size and shape are subject to certain restrictions, flexibility is poor.Powder metallurgy method often used for the production of hard alloy, antifriction material, structural material, friction material, refractory metal materials, filter materials, metal ceramic, no segregation in high speed tool steel, magnetic materials, heat resistant materials.
Key words:powder metallurgy, basic process, application, development trend, problems and opportunities
一基本简介
粉末冶金是制取金属或用金属粉末（或金属粉末与非金属粉末的混合物）作为原料，经过成形和烧结，制造金属材料、复合以及各种类型制品的工艺技术。
二发展前景
近年来，通过不断引进国外先进技术与自主开发创新相结合，中国粉末冶金产业和技术都呈现出高速发展的态势，是中国机械通用零部件行业中增长最快的行业之一，每年全国粉末冶金行业的产值以35%的速度递增。
全球制造业正加速向中国转移，汽车行业、机械制造、金属行业、航空航天、仪器仪表、五金工具、工程机械、电子家电及高科技产业等迅猛发展，为粉末冶金行业带来了不可多得的发展机遇和巨大的市场空间。另外，粉末冶金产业被中国列入优先发展和鼓励外商投资项目，发展前景广阔。
七、粉末冶金研究先进设备-放电等离子烧结系统（SPS）
1 前言
随着高新技术产业的发展，新型材料特别是新型功能材料的种类和需求量不断增加，材料新的功能呼唤新的制备技术。放电等离子烧结（Spark Plasma Sintering，简称SPS）是制备功能材料的一种全新技术，它具有升温速度快、烧结时间短、组织结构可控、节能环保等鲜明特点，可用来制备金属材料、陶瓷材料、复合材料，也可用来制备纳米块体材料、非晶块体材料、梯度材料等。
2 国内外SPS的发展与应用状况
SPS技术是在粉末颗粒间直接通入脉冲电流进行加热烧结，因此在有的文献上也被称为等离子活化烧结或等离子辅助烧结（plasmaactivatedsintering-PAS或
plasma-assistedsintering-PAS）[1,2]。早在1930年，美国科学家就提出了脉冲电流烧结原理，但是直到1965年，脉冲电流烧结技术才在美、日等国得到应用。日本获得了SPS技术的专利，但当时未能解决该技术存在的生产效率低等问题，因此SPS技术没有得到推广应用。
1988年日本研制出第一台工业型SPS装置，并在新材料研究领域内推广使用。1990年以后，日本推出了可用于工业生产的SPS第三代产品，具有10～100t 的烧结压力和
脉冲电流5000～8000A。最近又研制出压力达500t，脉冲电流为25000A的大型SPS装置。由于SPS技术具有快速、低温、高效率等优点，近几年国外许多大学和科研机构都相继配备了SPS烧结系统，并利用SPS进行新材料的研究和开发[3]。1998年瑞典购进SPS烧结系统，对碳化物、氧化物、生物陶瓷等材料进行了较多的研究工作[4]。
国内近三年也开展了用SPS技术制备新材料的研究工作[1,3]，引进了数台SPS烧结系统，主要用来烧结纳米材料和陶瓷材料[5～8]。SPS作为一种材料制备的全新技术，已引起了国内外的广泛重视。
3 SPS的烧结原理
3.1等离子体和等离子加工技术[9，10]
SPS是利用放电等离子体进行烧结的。等离子体是物质在高温或特定激励下的一种物质状态，是除固态、液态和气态以外，物质的第四种状态。等离子体是电离气体，由大量正负带电粒子和中性粒子组成，并表现出集体行为的一种准中性气体。
等离子体是解离的高温导电气体，可提供反应活性高的状态。等离子体温度4000～10999℃，其气态分子和原子处在高度活化状态，而且等离子气体内离子化程度很高，这些性质使得等离子体成为一种非常重要的材料制备和加工技术。
等离子体加工技术已得到较多的应用，例如等离子体CVD、低温等离子体PBD以及等离子体和离子束刻蚀等。目前等离子体多用于氧化物涂层、等离子刻蚀方面，在制备高纯碳化物和氮化物粉体上也有一定应用。而等离子体的另一个很有潜力的应用领域是在陶瓷材料的烧结方面[1]。
产成等离子体的方法包括加热、放电和光激励等。放电产生的等离子体包括直流放电、射频放电和微波放电等离子体。SPS利用的是直流放电等离子体。
3.2SPS装置和烧结基本原理
SPS装置主要包括以下几个部分：轴向压力装置；水冷冲头电极；真空腔体；气氛控制系统（真空、氩气）；直流脉冲及冷却水、位移测量、温度测量、和安全等控制单元。SPS的基本结构如图1所示。
SPS与热压（HP）有相似之处，但加热方式完全不同，它是一种利用通-断直流脉冲电流直接通电烧结的加压烧结法。通-断式直流脉冲电流的主要作用是产生放电等离子体、放电冲击压力、焦耳热和电场扩散作用[11]。SPS烧结时脉冲电流通过粉末颗粒如图2所示。在SPS烧结过程中，电极通入直流脉冲电流时瞬间产生的放电等离子体，使烧结体内部各个颗粒均匀的自身产生焦耳热并使颗粒表面活化。与自身加热反应合成法（SHS）和微波烧结法类似，SPS是有效利用粉末内部的自身发热作用而进行烧结的。SPS 烧结过程可以看作是颗粒放电、导电加热和加压综合作用的结果。除加热和加压这两个促进烧结的因素外，在SPS技术中，颗粒间的有效放电可产生局部高温，可以使表面局部熔化、表面物质剥落；高温等离子的溅射和放电冲击清除了粉末颗粒表面杂质（如去处表面氧化物等）和吸附的气体。电场的作用是加快扩散过程[1，9，12]。
4 SPS的工艺优势
SPS的工艺优势十分明显：加热均匀，升温速度快，烧结温度低，烧结时间短，生产效率高，产品组织细小均匀，能保持原材料的自然状态，可以得到高致密度的材料，可以烧结梯度材料以及复杂工件[3，11]。与HP和HIP相比，SPS装置操作简单，不需要专门的熟练技术。文献[11]报道，生产一块直径100mm、厚17mm的ZrO2(3Y)/不锈钢梯度材料（FGM）用的总时间是58min，其中升温时间28min、保温时间5min和冷却时间25min。与HP相比，SPS技术的烧结温度可降低100～200℃[13]。
5 SPS在材料制备中的应用
目前在国外，尤其是日本开展了较多用SPS制备新材料的研究，部分产品已投入生产。SPS可加工的材料种类如表1所示。除了制备材料外，SPS还可进行材料连接，如连接MoSi2与石磨[14]，ZrO2/Cermet/Ni等[15]。
近几年，国内外用SPS制备新材料的研究主要集中在：陶瓷、金属陶瓷、金属间化合物，复合材料和功能材料等方面。其中研究最多的是功能材料，他包括热电材料[16] 、磁性材料[17] 、功能梯度材料[18] 、复合功能材料[19]和纳米功能材料[20]等。对SPS 制备非晶合金、形状记忆合金[21] 、金刚石等也作了尝试，取得了较好的结果。
5 .1功能梯度材料
功能梯度材料（FGM）的成分是梯度变化的，各层的烧结温度不同，利用传统的烧结方法难以一次烧成。利用CVD、PVD等方法制备梯度材料，成本很高，也很难实现工业化。采用阶梯状的石磨模具，由于模具上、下两端的电流密度不同，因此可以产生温度梯度。利用SPS在石磨模具中产生的梯度温度场，只需要几分钟就可以烧结好成分配比不同的梯度材料。目前SPS成功制备的梯度材料有：不锈钢/ZrO2；Ni/ZrO2；Al/高聚物；Al/植物纤维；PSZ/T等梯度材料。
在自蔓延燃烧合成（SHS）中，电场具有较大激活效应和作用，特别是场激活效应可以使以前不能合成的材料也能成功合成，扩大了成分范围，并能控制相的成分，不过得到的是多孔材料，还需要进一步加工提高致密度。利用类似于SHS电场激活作用的SPS 技术，对陶瓷、复合材料和梯度材料的合成和致密化同时进行，可得到65nm的纳米晶，比SHS少了一道致密化工序[22]。利用SPS可制备大尺寸的FGM，目前SPS制备的尺寸较大的FGM体系是ZrO2(3Y)/不锈钢圆盘，尺寸已达到100mm×17mm[23]。
用普通烧结和热压WC粉末时必须加入添加剂，而SPS使烧结纯WC成为可能。用SPS 制备的WC/Mo梯度材料的维氏硬度（HV）和断裂韧度分别达到了24Gpa和6Mpa·m1/2,大大减轻由于WC和Mo的热膨胀不匹配而导致热应力引起的开裂[24]。
5 .2 热电材料
由于热点转换的高可靠性、无污染等特点，最近热电转换器引起了人们的极大兴趣，并研究了许多热电转换材料。经文献检索发现，在SPS制备功能材料的研究中，对热电材料的研究较多。
(1)热电材料的成分梯度化氏目前提高热点效率的有效途径之一。例如，成分梯度的βFeSi2就是一种比较有前途的热电材料，可用于200～900℃之间进行热电转换。
βFeSi2没有毒性，在空气中有很好的抗氧化性，并且有较高的电导率和热电功率。热点材料的品质因数越高（Z=α2/kρ，其中Z是品质因数，α为Seebeck系数，k为热导系数，ρ为材料的电阻率），其热电转换效率也越高。试验表明，采用SPS制备的成分梯度的βFeSix(Si含量可变)，比βFeSi2的热电性能大为提高[25]。这方面的例子还有Cu/Al2O3/Cu[26],MgFeSi2[27], βZn4Sb3[28],钨硅化物[]29]等。
(2)用于热电制冷的传统半导体材料不仅强度和耐久性差，而且主要采用单相生长法制备，生产周期长、成本高。近年来有些厂家为了解决这个问题，采用烧结法生产半导体致冷材料，虽改善了机械强度和提高了材料使用率，但是热电性能远远达不到单晶半导体的性能，现在采用SPS生产半导体致冷材料，在几分钟内就可制备出完整的半导体材料，而晶体生长却要十几个小时。SPS制备半导体热电材料的优点是，可直接加工成圆片，不需要单向生长法那样的切割加工，节约了材料，提高了生产效率。
热压和冷压-烧结的半导体性能低于晶体生长法制备的性能。现用于热电致冷的半导体材料的主要成分是Bi,Sb,Te和Se，目前最高的Z值为3.0×10/K，而用SPS制备的热电半导体的Z值已达到2.9～3.0×10/K，几乎等于单晶半导体的性能[30]。表2是SPS和其他方法生产BiTe材料的比较。
5 .3 铁电材料
用SPS烧结铁电陶瓷PbTiO3时，在900～1000℃下烧结1～3min,烧结后平均颗粒尺寸<1μm，相对密度超过98%。由于陶瓷中孔洞较少[31]，因此在101～106HZ之间介电常数基本不随频率而变化。
用SPS制备铁电材料Bi4Ti3O12陶瓷时，在烧结体晶粒伸长和粗化的同时，陶瓷迅速致密化。用SPS容易得到晶粒取向度好的试样，可观察到晶粒择优取向的Bi4Ti3O12陶瓷的电性能有强烈的各向异性[32]。
用SPS制备铁电Li置换IIVI半导体ZnO陶瓷，使铁电相变温度Tc提高到470K，而以前冷压烧结陶瓷只有330K[34]。
5 .4 磁性材料
用SPS烧结Nd Fe B磁性合金，若在较高温度下烧结，可以得到高的致密度，但烧结温度过高会导致出现温度过高会导致出现α相和晶粒长大，磁性能恶化。若在较低温度下烧结，虽能保持良好的磁性能，但粉末却不能完全压实，因此要详细研究密度与性能的关系[35] 。
SPS在烧结磁性材料时具有烧结温度低、保温时间短的工艺优点。Nd Fe Co V B 在650℃下保温5min,即可烧结成接近完全密实的块状磁体，没有发现晶粒长大[36]。用SPS制备的865Fe6Si4Al35Ni和MgFe2O4的复合材料（850℃，130MPa），具有高的饱和磁化强度Bs=12T和高的电阻率ρ=1×10Ω·m[37]。
以前用快速凝固法制备的软磁合金薄带，虽已达到几十纳米的细小晶粒组织，但是不能制备成合金块体，应用受到限制。而现在采用SPS制备的块体磁性合金的磁性能已达到非晶和纳米晶组织带材的软磁性能[3]。
5 .5 纳米材料
致密纳米材料的制备越来越受到重视。利用传统的热压烧结和热等静压烧结等方法来制备纳米材料时，很难保证能同时达到纳米尺寸的晶粒和完全致密的要求。利用SPS 技术，由于加热速度快，烧结时间短，可显著抑制晶粒粗化。例如：用平均粒度为5μm 的TiN粉经SPS烧结（1963K，196～382MPa，烧结5min），可得到平均晶粒65nm的TiN 密实体[3]。文献[3]中引用有关实例说明了SPS烧结中晶粒长大受到最大限度的抑制，所制得烧结体无疏松和明显的晶粒长大。
在SPS烧结时，虽然所加压力较小，但是除了压力的作用会导致活化能力Q降低外，由于存在放电的作用，也会使晶粒得到活化而使Q值进一步减小，从而会促进晶粒长大，因此从这方面来说，用SPS烧结制备纳米材料有一定的困难。
但是实际上已有成功制备平均粒度为65nm的TiN密实体的实例。在文献[38]中，非晶粉末用SPS烧结制备出20～30nm的Fe90Zr7B3纳米磁性材料。另外，还已发现晶粒随SPS烧结温度变化比较缓慢[7]，因此SPS制备纳米材料的机理和对晶粒长大的影响还需要做进一步的研究。
5. 6 非晶合金的制备
在非晶合金的制备中，要选择合金成分以保证合金具有极低的非晶形成临界冷却速度，从而获得极高的非晶形成能力。在制备工艺方面主要有金属浇铸法和水淬法，其关键是快速冷却和控制非均匀形核。由于制备非晶合金粉末的技术相对成熟，因此多年来，采用非晶粉末在低于其晶化温度下进行温挤压、温轧、冲击（爆炸）固化和等静压烧结等方法来制备大块非晶合金，但存在不少技术难题，如非晶粉末的硬度总高于静态粉末，因而压制性能欠佳，其综合性能与旋淬法制备的非晶薄带相近，难以作为高强度结构材料使用[39]。可见用普通粉末冶金法制备大块非晶材料存在不少技术难题。
SPS作为新一代烧结技术有望在这方面取得进展，文献[40]中利用SPS烧结由机械合金化制取的非晶Al基粉末得到了块状圆片试样（10mm×2mm），磁非晶合金是在375MPa 下503K时保温20min制备的，含有非晶相和结晶相以及残余的Sn相。其非晶相的结晶温度是533K。文献[41]中用脉冲电流在423K和500MPa下制备了Mg80Ni10Y5B5块状非晶合金，经分析其中主要是非晶相。非晶Mg合金比A291D合金和纯镁有较高的腐蚀电位和较低的腐蚀电流密度，非晶化改善了镁合金的抗腐蚀抗力。从实践来看，可以采用SPS烧结法制备块状非晶合金。因此利用先进的SPS技术进行大块非晶合金的制备研究很有必要。
6总结与展望
放电等离子烧结（SPS）是一种低温、短时的快速烧结法，可用来制备金属、陶瓷、纳米材料、非晶材料、复合材料、梯度材料等。SPS的推广应用将在新材料的研究和生产领域中发挥重要作用。
SPS的基础理论目前尚不完全清楚，需要进行大量实践与理论研究来完善，SPS需要增加设备的多功能性和脉冲电流的容量，以便做尺寸更大的产品；特别需要发展全自
动化的SPS生产系统，以满足复杂形状、高性能的产品和三维梯度功能材料的生产需要[42]。
对实际生产来说，需要发展适合SPS技术的粉末材料，也需要研制比目前使用的模具材料（石墨）强度更高、重复使用率更好的新型模具材料，以提高模具的承载能力和降低模具费用。
在工艺方面，需要建立模具温度和工件实际温度的温差关系，以便更好的控制产品质量。在SPS产品的性能测试方面，需要建立与之相适应的标准和方法。
三主要特点
粉末冶金具有独特的化学组成和机械、物理性能，而这些性能是用传统的熔铸方法无法获得的。运用粉末冶金技术可以直接制成多孔、半致密或全致密材料和制品，如含油轴承、齿轮、凸轮、导杆、刀具等，是一种少无切削工艺。
（1）粉末冶金技术可以最大限度地减少合金成分偏聚，消除粗大、不均匀的铸造组织。在制备高性能稀土永磁材料、稀土储氢材料、稀土发光材料、稀土催化剂、高温超导材料、新型金属材料（如Al-Li合金、耐热Al合金、超合金、粉末耐蚀不锈钢、粉末高速钢、金属间化合物高温结构材料等）具有重要的作用。
（2）可以制备非晶、微晶、准晶、纳米晶和超饱和固溶体等一系列高性能非平衡材料，这些材料具有优异的电学、磁学、光学和力学性能。
（3）可以容易地实现多种类型的复合，充分发挥各组元材料各自的特性，是一种低成本生产高性能金属基和陶瓷复合材料的工艺技术。
（4）可以生产普通熔炼法无法生产的具有特殊结构和性能的材料和制品，如新型多孔生物材料，多孔分离膜材料、高性能结构陶瓷磨具和功能陶瓷材料等。
（5）可以实现近净形成形和自动化批量生产，从而，可以有效地降低生产的资源和能源消耗。
（6）可以充分利用矿石、尾矿、炼钢污泥、轧钢铁鳞、回收废旧金属作原料，是一种可有效进行材料再生和综合利用的新技术。
我们常见的机加工刀具，五金磨具，很多就是粉末冶金技术制造的。
四应用分类
（1）应用：（汽车、摩托车、纺织机械、工业缝纫机、电动工具、五金工具。电器.工程机械等）各种粉末冶金（铁铜基）零件。[1]
（2）分类：粉末冶金多孔材料、粉末冶金减摩材料、粉末冶金摩擦材料、粉末冶金结构零件、粉末冶金工模具材料、和粉末冶金电磁材料和粉末冶金高温材料等。
五生产过程
（1）生产粉末。粉末的生产过程包括粉末的制取、粉料的混合等步骤。为改善粉末的成型性和可塑性通常加入机油、橡胶或石蜡等增塑剂。
（2）压制成型。粉末在15-600MPa压力下，压成所需形状。[2]
（3）烧结。在保护气氛的高温炉或真空炉中进行。烧结不同于金属熔化，烧结时至少有一种元素仍处于固态。烧结过程中粉末颗粒间通过扩散、再结晶、熔焊、化合、溶解等一系列的物理化学过程，成为具有一定孔隙度的冶金产品。
（4）后处理。一般情况下，烧结好的制件可直接使用。但对于某些尺寸要求精度高并且有高的硬度、耐磨性的制件还要进行烧结后处理。后处理包括精压、滚压、挤压、淬火、表面淬火、浸油、及熔渗等。
六工艺性能
等静压成型粉末冶金
金属喷射成型粉末冶金
粉末锻造粉末冶金
压力烧结粉末冶金
粉末性能(property of powder)
粉末所有性能的总称。它包括：粉末的几何性能(粒度、比表面、孔径和形状等)；粉末的化学性能(化学成分、纯度、氧含量和酸不溶物等)；粉体的力学特性(松装密度、流动性、成形性、压缩性、堆积角和剪切角等)；粉末的物理性能和表面特性(真密度、光泽、吸波性、表面活性、ze%26mdash;ta(%26ccedil;)电位和磁性等)。粉末性能往往在很大程度上决定了粉末冶金产品的性能。
几何性能最基本的是粉末的粒度和形状。
(1)粒度。它影响粉末的加工成形、烧结时收缩和产品的最终性能。某些粉末冶金制品的性能几乎和粒度直接相关，例如，过滤材料的过滤精度在经验上可由原始粉末颗粒的平均粒度除以10求得；硬质合金产品的性能与wc相的晶粒有很大关系，要得到较细晶粒度的硬质合金，惟有采用较细粒度的wc原料才有可能。生产实践中使用的粉末，其粒度范围从几百个纳米到几百个微米。粒度越小，活性越大，表面就越容易氧化和吸水。当小到几百个纳米时，粉末的储存和输运很不容易，而且当小到一定程度时量子效应开始起作用，其物理性能会发生巨大变化，如铁磁性粉会变成超顺磁性粉，熔点也随着粒度减小而降低。
(2)粉末的颗粒形状。它取决于制粉方法，如电解法制得的粉末，颗粒呈树枝状；还原法制得的铁粉颗粒呈海绵片状；气体雾化法制得的基本上是球状粉。此外，有些粉末呈卵状、盘状、针状、洋葱头状等。粉末颗粒的形状会影响到粉末的流动性和松装密
度，由于颗粒间机械啮合，不规则粉的压坯强度也大，特别是树枝状粉其压制坯强度最大。但对于多孔材料，采用球状粉最好。
力学特性粉末的力学性能即粉末的工艺性能，它是粉末冶金成形工艺中的重要工艺参数。粉末的松装密度是压制时用容积法称量的依据；粉末的流动性决定着粉末对压模的充填速度和压机的生产能力；粉末的压缩性决定压制过程的难易和施加压力的高低；而粉末的成形性则决定坯的强度。
化学性能主要取决于原材料的化学纯度及制粉方法。较高的氧含量会降低压制性能、压坯强度和烧结制品的力学性能，因此粉末冶金大部分技术条件中对此都有一定规定。例如，粉末的允许氧含量为0.2%～1.5%，这相当于氧化物含量为1%～10%。
参考文献：
【1】粉末冶金新技术与新装备刘文胜马运柱... 矿冶工程 2007 5
【2】现代粉末冶金材料和技术发展现状（一）黄伯云易健宏上海金属 2007 3
【3】现代粉末冶金材料和技术发展现状（二）黄伯云易健宏上海金属 2007 4
【4】钛及钛合金的粉末冶金新技术周洪强陈志强材料导报：网络版 2006 1
【5】世界粉末冶金的发展现状刘咏黄伯云中国有色金属2006 1
【6】粉末冶金多孔材料性能研究孙纪国王浩... 导弹与航天运载技术 2006 4
【7】粉末冶金文摘亓家钟（摘择）粉末冶金技术 2006 2
【8】German R M. Powder Inject ion Molding [ M] . MPIF: Princeton,1990. 61~ 95.
【9】Capus J, Pickering S, Weaver A. Hoeganaes offers higher density atlower cost [ J] . Metal Powder Report, 1994, 49 ( 78) : 22~ 24.
【10】 Rutz H G, Hanejko F G. High density processing of high
performance ferrous mat erials [ J ] . The Internat ional of PowderMetallurgy, 1995, 31 ( 1) : 9~ 17.
材料工艺课程论文
浮玻璃工艺研究 【摘要】本文主要介绍的是浮法玻璃的生产工艺。浮法玻璃生产系统是在锡液上漂浮连续成型的较大型玻璃生产系统。一个浮法玻璃厂的主要系统主要分为原料配料系统、熔窑系统、锡槽系统、退火窑系统等。 【关键词】浮法玻璃；配料；融化；锡槽；退火。
引言 我们知道,浮法玻璃工艺是利用熔融玻璃液连续流到并漂浮在比重大的金属锡液面上,玻璃液在高温一下借助于金属锡液和玻璃液的表面张力、玻璃液与金属锡液的界面张力以及玻璃重力的共同作用,使玻璃液在锡液面上铺开、摊平,形成上下表面平整、无波筋以及相互平行的玻璃带,玻璃带在锡槽内逐渐冷却降温硬化后脱离锡液面,经玻璃退火册断册边切裁,就能得到用浮法工艺生产出的平板玻璃产品。一般的生产流程分四个系统。分别为配料系统、融化系统、成型切割、退火系统。 一、配料系统 1.1玻璃成分 玻璃的成分包括SiO2 、Al2O3 、CaO、MgO、Na2O和K2O。由于一些原料有其特殊之处，所以在各个工序中都要对其加以克服才能顺利而又合理的制作出合乎要求的玻璃。由于SiO2的熔点过高，大约在1710℃，所以就要加入适量的CaO和K2O来降低熔点，而这两种原料都相对比较贵，容易提高制作成本，就适量加一些Al2O3，还有其他的一些原料加入，都有其中的用意，每一种原料的加入都是有原因的。 1.2玻璃原料 主要有：石英砂、石灰石、长石、纯碱、硼酸等。辅助原料：着色剂金属氧化物。助熔剂：萤石CaF2 。澄清剂：碳。 1.3配料方案 按照浮法玻璃生产线的工艺要求，配料现场需要石英砂、长石、石灰石、白云石、纯碱、芒硝、碳粉、铁粉、碎玻璃等九种主要原材料的供应仓。原料从砂矿运来工厂首先分产地分批次在均化库里均化。均化后按照计算配比称量，由混
粉末冶金的烧结技术
粉末冶金的烧结技术 作者：本站整理文章来源：本站搜集点击数：466 更新时间：2008-3-17 16:03:20 1.烧结的方法 不同的产品、不同的性能烧结方法不一样。 ⑴按原料组成不同分类。可以将烧结分为单元系烧结、多元系固相烧结及多元系液相烧结。 单元系烧结是纯金属（如难熔金属和纯铁软磁材料）或化合物(Al2O3、B4C、BeO、M oSi2等)熔点以下的温度进行固相烧结。多元系固相烧结是由两种或两种以上的组元构成的烧结体系，在其中低熔成分的熔点温度以下进行的固相烧结。粉末烧结合金多属于这一类。如Cu-Ni、Fe-Ni、Cu-Au、W-Mo、Ag-Au、Fe-Cu、W-Ni、Fe-C、Cu-C、Cu-W、Ag -W等。多元系液相烧结以超过系统中低熔成分熔点的温度进行的烧结。如W-Cu-Ni、W-Cu、WC-Co、TiC-Ni、Fe-Cu(Cu>10%、Fe-Ni-Al、Cu-Pb、Cu-Sn、Fe-Cu(Cu<10%)等 ⑵按进料方式不同分类。分为为连续烧结和间歇烧结。 连续烧结 烧结炉具有脱蜡、预烧、烧结、制冷各功能区段，烧结时烧结材料连续地或平稳、分段地完成各阶段的烧结。连续烧结生产效率高，适用于大批量生产。常用的进料方式有推杆式、辊道式和网带传送式等。
间歇烧结 零件置于炉内静止不动，通过控温设备，对烧结炉进行需要的预热、加热及冷却循环操作，完成烧结材料的烧结过程。间歇烧结可依据炉内烧结材料的性能确定合适的烧结制度，但生产效率低，适用于单件、小批量生产，常用的烧结炉有钟罩式炉、箱式炉等。 除上述分类方法外。按烧结温度下是否有液相分为固相烧结和液相烧结；按烧结温度分为中温烧结和高温烧结（1100～1700℃），按烧结气氛的不同分为空气烧结，氢气保护烧结（如钼丝炉、不锈钢管和氢气炉等）和真空烧结。另外还有超高压烧结、活化热压烧结等新的烧结技术。 2.影响粉末制品烧结质量的因素 影响烧结体性能的因素很多，主要是粉末体的性状、成形条件和烧结的条件。烧结条件的因素包括加热速度、烧结温度和时间、冷却速度、烧结气氛及烧结加压状况等。 ⑴烧结温度和时间 烧结温度的高低和时间的长短影响到烧结体的孔隙率、致密度、强度和硬度等。烧结温度过高和时间过长，将降低产品性能，甚至出现制品过烧缺陷；烧结温度过低或时间过短，制品会因欠烧而引起性能下降。 ⑵烧结气氛
粉末冶金生产的基本工艺流程
转贴]粉末冶金生产的基本工艺流程 标签：转贴粉末冶金生产基本工艺流程时间：2008-11-26 21:23:53 点击：2803 回帖：0 上一篇：[转贴]金属磨损自修复抗磨剂的性下一篇：金相显微镜的外形尺寸图(图) 粉末冶金生产的基本工艺流程包括：粉末制备、粉末混合、压制成形、烧结及后续处理等。用简图表示于图7-1中。陶瓷制品的生产过程与粉末冶金有许多相似之处，其工艺过程包括粉末制备、成形和致密化三个阶段。 2．1 粉末制备 2．1．1 粉末制备 粉末是制造烧结零件的基本原料。粉末 的制备方法有很多种，归纳起来可分为机械 法和物理化学法两大类。 （1）机械法机械法有机械破碎法与液 态雾化法。 机械破碎法中最常用的是球磨法。该法 用直径10~20mm钢球或硬质合金对金属进行 球磨，适用于制备一些脆性的金属粉末（如 铁合金粉）。对于软金属粉，采用旋涡研磨 法。 雾化法也是目前用得比较多的一种机械 制粉方法，特别有利于制造合金粉，如低合 金钢粉、不锈钢粉等。将熔化的金属液体通 过小孔缓慢下流，用高压气体（如压缩空气） 或液体（如水）喷射，通过机械力与急冷作 用使金属熔液雾化。结果获得颗粒大小不同的金属粉末。图7-2为粉末气体雾化示意图。雾化法工艺简单，可连续、大量生产，而被广泛采用。
（2）物理化学法常见的物理方法有气相与液相沉 积法。如锌、铅的金属气体冷凝而获得低熔点金属粉末。 又如金属羰基物Fe(CO)5、Ni(CO)4等液体经180~250℃ 加热的热离解法，能够获得纯度高的超细铁与镍粉末， 称为羰基铁与羰基镍。 化学法主要有电解法与还原法。电解法是生产工业 铜粉的主要方法，即采用硫酸铜水溶液电解析出纯高的 铜。还原法是生产工业铁粉的主要方法，采用固体碳还 原铁磷或铁矿石粉的方法。还原后得到得到海绵铁，经 过破碎后的铁粉在氢气气氛下退火，最后筛分便制得所 需要的铁粉。图7-2 粉末气体雾化示意图 2．1．2 粉末性能 粉末的性能对其成形和烧结过程，及制品的性能都有重大影响，因而对粉末的性能必须加以了解。粉末的性能可分为物理性能、化学性能和工艺性能。物理性能有颗粒形状、粒度及粒度组成、密度、硬度、加工硬化性、塑性变形能力以及显微组织等；化学性能有化学成分；工艺性能有粉末的松装密度、流动性和压制性等。通常用下述几个主要性能来评价粉末的性能。 （1）颗粒形状、粒度及粒度组成 a．颗粒形状颗粒形状是决定粉末工艺性能的主要因素。用不同方法制造的粉末形状不同，如表7-2所示。颗粒的形状如图7-3所示。颗粒形状对粉末的压制成形和烧结都会带来影响。如表面光滑的粉末颗粒，其流动性好，对提高压坯的密度有利。但形状复杂的粉末，对提高制品的压坯强度有利，同时能促进烧结的进行。 表7-2 颗粒形状、松装密度与粉末生产方法的关系 粉末生产方法 粉末颗粒形状 松装密度g/cm3 粉末生产方法
材料工艺学课程设计.
材料工艺学课程设计(论文) 题目：Cr12MoV钢电动机硅钢片冲裁模球化退火-淬火- 回火工艺设计 院（系）： 专业班级： 学号： 学生姓名： 指导教师： 教师职称： 起止时间：
课程设计（论文）任务及评语 院（系）：材料科学与工程学院教研室：材料科学与工程学号学生姓名专业班级 课程设计 （论文） 题目 Cr12MoV钢电动机硅钢片冲裁模球化退火-淬火-回火热处理工艺设计 课程设计（论文）要求与任务一、课设要求 熟悉设计题目，查阅相关文献资料，概述相关工件的热处理工艺，进行工件的服役条件与失效形式分析，提出硬度、耐磨性、强度等要求，完成工艺设计。阐述Cr12MoV电动机硅钢片冲裁模球化退火-淬火-回火热处理工艺理论基础，选择设备、仪表和工夹具，阐述电动机硅钢片冲裁模热处理质量检验项目、内容及要求；阐明电动机硅钢片冲裁模热处理常见缺陷的预防及补救方法；给出所用参考文献。 二、课设任务 1.电动机硅钢片冲裁模材料的选择（要求在满足工件使用性能的前提下，兼顾经济性和工艺性，合理选择材料）； 2.给出Cr12MoV的C曲线； 3.给出Cr12MoV电动机硅钢片冲裁模冷热加工工艺流程图； 4.制定Cr12MoV电动机硅钢片冲裁模球化退火-淬火-回火热处理工艺 三、设计说明书要求 设计说明书包括三部分：1）概述；2）工艺设计；3）热处理工艺卡；4）参考文献。设计说明书结构见《工艺设计模板》。 工作计划 集中学习0.5天，资料查阅与学习，讨论1.5天，设计7天：1）概述0.5天，2）服役条件与性能要求0.5天，3）失效形式、材料的选择0.5天，4）结构形状与热处理工艺性0.5天，5）冷热加工工序安排0.5天，6）工艺流程图0.5天，7）热处理工艺设计2天，8）工艺的理论基础、原则0.5天，9）设计工夹具0.5天，10）可能出现的问题分析及防止措施0.5天，11）热处理质量分析0.5天，设计验收1天。 指 导 教 师 评 语 及 成 绩 成绩：指导教师签字： 年月日
粉末冶金技术论文..
粉末冶金技术 摘要：粉末冶金是制取金属或用金属粉末（或金属粉末与非金属粉末的混合物）作为原料，经过成形和烧结，制造金属材料、复合以及各种类型制品的工艺技术。粉末冶金法与生产陶瓷有相似的地方，因此，一系列粉末冶金新技术也可用于陶瓷材料的制备。粉末冶金材料是指用几种金属粉末或金属与非金属粉末作原料，通过配料、压制成形、烧结等工艺过程而制成的材料。这种工艺过程成为粉末冶金法，是一种不同于熔炼和铸造的方法。其生产过程与陶瓷制品相类似，所以又称金属陶瓷法。粉末冶金法不仅是制取具有某些特殊性能材料的方法，也是一种无切削或少切削的加工方法。它具有生产率高、材料利用率高、节省机床和生产占地面积等优点。但金属粉末和模具费用高，制品大小和形状受到一定限制，制品的韧性较差。粉末冶金法常用于制作硬质合金、减摩材料、结构材料、摩擦材料、难熔金属材料、过滤材料、金属陶瓷、无偏析高速工具钢、磁性材料、耐热材料等。 关键词：粉末冶金、基本工序、应用、发展方向、问题及机遇 Powder metallurgy technology (11 grade material class two) Abstract:Powder metallurgy is used for preparing metal or metal powder (or metal powder and metal powder mixture) as raw material, after forming and sintering, manufacture of metal materials, composite and various types of products technology.Powder metallurgy method and the production of ceramic have similar place, therefore, a series of new powder metallurgy technologies can also be used for preparing ceramic material. Powder metallurgy materials refers to the use of several kinds of metal powder or metal and non metal powder as raw material, through mixing, pressing, sintering process and made of materials.The process to become powder metallurgy method, is different from the melting and casting method.Its production process and ceramic products are similar, so called ceramic metal.Powder metallurgy method not only has some special properties of material preparation method, is also a kind of without cutting or less cutting processing method. It has high productivity, high material utilization rate, saving machine tools and production area etc..But the metal powder and high mold cost, product size and shape are subject to certain restrictions, flexibility is poor.Powder metallurgy method often used for the production of hard alloy, antifriction material, structural material, friction material, refractory metal materials, filter materials, metal ceramic, no segregation in high speed tool steel, magnetic materials, heat resistant materials. Key words:powder metallurgy, basic process, application, development trend, problems and opportunities
粉末冶金工艺基本知识
粉末冶金工艺基本知识 粉末冶金成形 粉末冶金工艺及材料 粉末冶金是制取金属粉末并通过成形和烧结等工艺将金属粉末或与非金属粉末的混合物制成制品的加工方法，既可制取用普通熔炼方法难以制取的特殊材料，又可制造各种精密的机械零件，省工省料。但其模具和金属粉末成本较高，批量小或制品尺寸过大时不宜采用。粉末冶金材料和工艺与传统材料工艺相比，具有以下特点： 1．粉末冶金工艺是在低于基体金属的熔点下进行的，因此可以获得熔点、密度相差悬殊的多种金属、金属与陶瓷、金属与塑料等多相不均质的特殊功能复合材料和制品。 2．提高材料性能。用特殊方法制取的细小金属或合金粉末，凝固速度极快、晶粒细小均匀，保证了材料的组织均匀，性能稳定，以及良好的冷、热加工性能，且粉末颗粒不受合金元素和含量的限制，可提高强化相含量，从而发展新的材料体系。 3．利用各种成形工艺，可以将粉末原料直接成形为少余量、无余量的毛坯或净形零件，大量减少机加工量。提高材料利用率，降低成本。 粉末冶金的品种繁多，主要有：钨等难熔金属及合金制品；用Co、Ni等作粘结剂的碳化钨（WC）、碳化钛（TiC）、碳化钽（TaC）等硬质合金，用于制造切削刀具和耐磨刀具中的钻头、车刀、铣刀，还可制造模具等；Cu合金、不锈钢及Ni等多孔材料，用于制造烧结含油轴承、烧结金属过滤器及纺织环等。随着粉末冶金生产技术的发展，粉末冶金及其制品将在更加广泛的应用。 1 粉末冶金基础知识 ⒈1 粉末的化学成分及性能 尺寸小于1mm的离散颗粒的集合体通常称为粉末，其计量单位一般是以微米（μm）或纳米（nm）。 1.粉末的化学成分 常用的金属粉末有铁、铜、铝等及其合金的粉末，要求其杂质和气体含量不超过1%～2%，否则会影响制品的质量。 2.粉末的物理性能 ⑴ 粒度及粒度分布 粉料中能分开并独立存在的最小实体为单颗粒。实际的粉末往往是团聚了的颗粒，即二次颗粒。图描绘了由若干一次颗粒聚集成二次颗粒的情形。实际的粉末颗粒体中不同尺寸所占的百分比即为粒度分布。 ⑵ 颗粒形状 即粉末颗粒的外观几何形状。常见的有球状、柱状、针状、板状和片状等，可以通过显微镜的观察确定。 ⑶ 比表面积 即单位质量粉末的总表面积，可通过实际测定。比表面积大小影响着粉末的表面能、表面吸附及凝聚等表面特性。 3.粉末的工艺性能 粉末的工艺性能包括流动性、填充特性、压缩性及成形性等。 ⑴ 填充特性 指在没有外界条件下，粉末自由堆积时的松紧程度。常以松装密度或堆积密度表示。粉末
模具制造工艺课程论文
模具制造工艺课程论文 班级：10材控2班学号：1010121136 姓名：赵佳伟 摘要：在现代生产中，模具已成为大批量生产各种工业产品和日用生活品的重要工艺装备。应用模具的目的在于保证产品的质量，提高生产率，并且降低生产成本。所以模具工业已成为世界上不可忽视的产业，而模具工业的发展将与我们的生活、工作息息相关。模具工业的发展关键是模具技术的发展。由此这篇文章将浅显的分析当今国内外模具工业的发展现状，其中也包括了模具工业的市场。并且较为初步的介绍了我国模具技术的现状和现代模具工业的特点。浅谈了模具技术发展的八大趋势。 关键词：模具; 模具工业模具技术现状发展趋势 1 引言 模具作为重要的工艺装备，在消费品、电器电子、汽车、飞机制造等工业部门有举足轻重的地位。工业产品零件粗加工的75%、精加工的50%及塑料零件的90%将由模具完成。我国模具行业近年来均增长速度为21%。今后一段时期，对模具的需求主要集中在四个行业：汽车行业、家用电器行业、电子及通讯行业和建材行业。模具是“效益放大器”，用模具生产的最终产品的价值要比模具自身的价值高几十倍。如汽车行业，目前我国汽车产量超过400万辆，基本车型达到170种，新车型和改装车型将达430种，汽车换型是约有80%的模具需要更换，一个型号的汽车所需模具达数千副，价值上亿元；家用电器行业中彩电、电冰箱、洗衣机、空调器、微波炉、录像机、摄影机、VCD、DVD等需用模具量大。单台彩电需用模具约140副。价值700万元。目前，全世界模具年产值约为600亿美元，日、美等工业发达国家的模具工业产值已超过机床工业，从1997年开始，我国模具工业产值也超过了机床工业产值。模具生产技术水平的高低，已成为衡量一个国家产品制造水平高低的重要标志，因为模具在很大程度上决定着产品的质量、效益和新产品的开发能力。模具行业日益受到国家和人们的关注和重视，国务院颁布的《关于当前产业政策的决定》也把模具行业列为机械制造工业改造序列的第一位。1999年8月20日党中央和国务院发布的《关于加强技术创新发展高科技实现产业化的决定》中，明确提出了高新技术产业领域。《决定》指出：要在电子信息特别是集成电路设计与制造、网络及通信、计算机及软件、数字化电子产品等方面，在生物技术及新医药、新技术、新能源、航空航天、海洋等有一定基础的高新技术产业领域，加强技术创新，形成一大批拥有自主知识产权、具有竞争优势的高新技术产业。在发布《决定》之前，1999年7月，国家计委和科学技术部发布了《当前国家优先发展的高新技术产业化重点领域指南(目录)》，《指南》中列入了电子专用模具、塑料成形新技术与新设备、快速原型制造工艺及成套设备、激光加工技术及成套设备、汽车关键零部件等。例如，采用快速原型制造技术和设备，用分层实体堆积等方法，可以将复杂的CAD模型转化为实物，使模具和产品的设计、评价与制造周期大大缩短，企业就能快速抢占市场，取得竞争优势。 2 模具工业的概述
粉末冶金技术
粉未治金技术 金属注射成形技术（MIM）由陶瓷零件的粉末注射成形技术发展而来，是一种新型的粉末冶金近净成形技术。MIM 技术的主要生产步骤如下： 金属粉末与粘结剂混合——制粒——注射成形——脱脂——烧结——后续处理——最终产品 该技术适用于大批量生产性能高、形状复杂的小尺寸的粉末冶金零部件。近几十年来，MIM技术发展势头迅猛，能应用的材料体系包括：Fe-Ni合金、不锈钢、工具钢、高比重合金、硬质合金、钛合金、镍基超合金、金属间化合物、氧化铝、氧化锆等。目前注射成形技术在国外已经有不少大规模的产业化应用，如瑞士的手表业。而国内近年来也已经涌现出不少具有一定实力MIM产品的生产企业，如中南工大的湖南英捷，北京安泰，山东乳山金珠以及上海富驰等。 金属和陶瓷粉末材料注射成型(粉末注射成型-PIM)作为一种有竞争力的技术，已经在精密零件领域确立了其地位。PIM的成功来自于塑料注射成型技术和粉末技术的组合，前者具有获得形状的高自由度；后者提供很宽的选择材料的可能性。这导致了形成一个年增长率高于20%的强有力的增长中的市场。粉末注射成型是一种接近纯塑造的加工方法，它组合了粉末技术和塑料注射成型技术的各种优势。聚合物注射成型的主要优点是高速和自动化地生产大批量、几何形状复杂而又无需进行重要的后修饰零件的可能性。PIM加工过程现在可以加工几乎所有可得到的、以适当的粉末形式存在的材料，包括金属、陶瓷、硬质合金、金属间化合物和复合材料。在粉末注射成型中，金属或陶瓷粉通过与足量的聚合物和蜡(粘接剂)混合和均化形成注射成型混合物，这种原料有聚合物的流动性质，能作为粒料用通常的注射成型方法进行加工。注射成型零件(绿色坯块)用如同塑料注射成型那样的方法成型，并采用或多或少有点复杂的注射成型模具。为了得到成品，粘接剂通常在一个两级加工过程中，借助热效应和/或一种化学过程，被从绿色坯块中除去(称谓脱粘接剂)。所形成的"褐色坯块"与注射成型零件有大致相同的形状和尺寸。但由于已经除去粘接剂，所以是一个多孔结构的零件。此零件然后在大约85%的熔点温度，在一个适当地调节好的环境中烧结。孔通过液相的扩散、成型，和颗料增大等而封闭。在烧结过程中零件形状完全保持，结果是用塑料成型加工法可得到的复杂的形状也能在金属和陶瓷零件上再现。精细的原料粉和光洁的模具表面可保证PIM加工方法具有突出的表面质量。按照用途的不同，烧结好的零件可在随后的产品后处理工序中，用搭接、研磨、机械、化学抛光、涂布等方法达到最终的、准备好供使用的状况。注射成型是确定几何形状和尺寸的关键工序。就像热塑性塑料情况那样，来自注料道和流道的混合料冷料可以再行造粒和回收使用，或者可采用热流道喷嘴，直接注射入零件。 零件尺寸从2 mm到5 cm PIM加工方法的典型应用是生产相对较小、密实而又形状复杂的零件，对它们的需求数量，每年在几千到几百万之间。它的高成型自由度使早先用几个工序生产或用几个零件装备起来形成的零件可用一个单独的PIM零件代替。有内部螺纹的、有难于加工的侧陷槽的、要求高表面质量的零件也能可靠地和自动化地进行生产。对于PIM零件，存在有一系列设计判据。PIM零件的典型的和经济上有吸引力的尺寸范围大约从2 mm到5 cm。紧固元件，如眼孔、螺纹或拉钩被集成到零件上也是很典型的，零件也包括，如齿轮、滑动螺栓、滑动表面、传动夹头或结构轴等结构元件。PIM特别适于制造有多功能特点的零件，成型自由度高，这大大扩展了传统生产工艺的适用范围，并且不需要复杂的机械修整和连接加工。 在许多生活领域中的应用PIM零件现在用于很多日常生活领域，如汽车和空间工业、化学工业、办公室设备和计算机工业，但也用于医药技术、运动设备和军事装备。例如厨房搅拌器的驱动托架，用不锈钢制成，重量为135g，这是一个相对较重的PIM零件。汽车点火开关盖以Fe2Ni为材料，由Radevormwald 的GKN Sinter Metals公司大批量生产。这种零件重8.8g，烧结后牢固地镀上铬。Dornstetten 的Klaeger公司批量生产的陶瓷杯，可省去固定把手的复杂工作程序。其他在消费品和宝石行业的著名的应用例子是不锈钢、钛和贵金属手表零件，例如由瑞士Grenchen的ETA公司生产的这类零件。注射成型机制造商Arburg公司采用了气体辅助技术，使中空的、重量轻的零件进入PIM加工过程。 世界范围的销售额为7亿美元简单概括一下PIM技术的历史发展情况，与PIM有关的第一个商业活动发生在1960年。但只是在过去的15年里，接受程度和市场潜力才取得稳定的增长。这一技术成熟到这种程度，它成为
粉末冶金基础知识
安全管理编号：LX-FS-A81397 粉末冶金基础知识 In the daily work environment, plan the important work to be done in the future, and require the personnel to jointly abide by the corresponding procedures and code of conduct, so that the overall behavior or activity reaches the specified standard 编写：_________________________ 审批：_________________________ 时间：________年_____月_____日 A4打印/ 新修订/ 完整/ 内容可编辑
粉末冶金基础知识 使用说明：本安全管理资料适用于日常工作环境中对安全相关工作进行具有统筹性，导向性的规划，并要求相关人员共同遵守对应的办事规程与行动准则，使整体行为或活动达到或超越规定的标准。资料内容可按真实状况进行条款调整，套用时请仔细阅读。 （一）粉末的化学成分及性能 尺寸小于1mm的离散颗粒的集合体通常称为粉末，其计量单位一般是以微米（μm）或纳米（nm）。 1.粉末的化学成分 常用的金属粉末有铁、铜、铝等及其合金的粉末，要求其杂质和气体含量不超过1%～2%，否则会影响制品的质量。 2.粉末的物理性能 ⑴粒度及粒度分布 粉料中能分开并独立存在的最小实体为单颗粒。
实际的粉末往往是团聚了的颗粒，即二次颗粒。实际的粉末颗粒体中不同尺寸所占的百分比即为粒度分布。 ⑵颗粒形状即粉末颗粒的外观几何形状。常见的有球状、柱状、针状、板状和片状等，可以通过显微镜的观察确定。 ⑶比表面积 即单位质量粉末的总表面积，可通过实际测定。比表面积大小影响着粉末的表面能、表面吸附及凝聚等表面特性。 3.粉末的工艺性能 粉末的工艺性能包括流动性、填充特性、压缩性及成形性等。 ⑴填充特性 指在没有外界条件下，粉末自由堆积时的松紧程
设计材料与加工工艺课程作业论文正稿
《水深火热》电磁炉 ———设计材料及加工工艺 学院艺术学院 学生倪搏学号 0104511 专业工业设计届别 10 届 指导教师柳献忠职称讲师 二O一二年十二月
摘要 创建于1968年的美的集团，是一家以家电业为主，涉足房产、物流等领域的大型综合性现代化企业集团，是中国最具规模的家电生产基地和出口基地，造型审美是人对产品的基本需要之一，但是现实对工业设计的要求早已超过了以美学为基础的外观造型的围。从工业革命以来，出现了大量机器工具，其基本设计思想是机器的功能和生产效率，并没有把操作者放在首位，迫使人的操作要适应机器的速度、强度和行为方式，造成了“以机器为本”的设计思想。在工业设计的畴，材料是指用于工业设计并且不依赖人的意识而存在的所有物质，因此设计材料所涉及的围十分广泛，从气态、液态到固态，从简单到化学物，无论是传统材料还是现在材料，无论是天然材料还是人工材料，无论是单一材料还是复合材料，均是设计的物质基础。 【关键词】外观造型功能材料
目录 1.电磁炉的发展历史 (4) 1.1早期的炉灶 (4) 1.2中期的炉灶 (5) 1.3现在的炉灶 (5) 1.4电磁炉的发展历史............................. 错误!未定义书签。 1.5电磁炉 (5) 1.6电磁炉的使用................................. 错误!未定义书签。 1.7中国电磁炉的发展 (5) 2电磁炉的结构........................... 错误!未定义书签。 2.1电磁炉的结构 (7) 2.11电磁炉整机零件介绍 (7) 2.12电磁炉主要部件讲解 (6) 2.2电磁炉工作原理 (6) 2.3电磁炉加热电路方框图 (7) 2.4.电磁炉的组成部分 (7) 2.5电磁炉的分类 (8) 3.电磁炉的特性 (8) 3.1电磁炉的优缺点 (8) 3.2电磁炉的保养 (8) 4电磁炉十大品牌排行榜 (8) 5设计材料的分类 (9) 5.1按材料的来源分类： (10) 5.2按材料的物质结构分类： (10) 5.3按材料的形态分类： (10) 5.4外壳材料 (10) 5.5面板的材料 (10) 5.6IGBT的材料 (10) 5.7固定线圈支架的选材 (11) 6加工工艺的分析 (11) 6.1压力铸造 (13) 6.2冲压成型 (13) 6.3铸塑成型 (13) 6.4熔融压制成型 (14) 7电磁炉的包装 (11) 7.1塑料薄膜包装袋： (13)
国内外关于粉末冶金机械零件——技术标准
国内外关于粉末冶金机械零件 材料的一些技术标准 滑动轴承粉末冶金轴承技术条件 （中华人民共和国国家标准GB2688-81） 本标准适用于GB2685-81《粉末冶金筒形轴承型式、尺寸与公差》、GB2686-81《粉末冶金带挡边筒形轴承型式、尺寸与公差》及GB2687-81《粉末冶金球形轴承型式、尺寸与公差》所规定的粉末冶金铁基和钢基轴承（以下简称轴承）。 1.技术要求 1.1轴承的材料按合金成分与密度分类规定于表1。 表1 材料牌号标记实例
铁基1类含油密度为5.7~6.28/cm3的粉末冶金轴承材料标记； 1.2轴承化学成分与物理一机械性能应符合表2规定。 1.3轴承的机构型式、尺寸与公差应符合GB2685-81、GB2686-81及GB2687-81的规定。 1.4轴承外观应有均匀的金属光泽，不允许有裂纹、夹杂和锈蚀等缺陷。 1.5轴承成品应浸渍的润滑油。一般浸渍GB443-64规定的HJ-20牌号机械油（铁基轴承允许加入防锈剂）。如对于浸渍的润滑油另有要求，应在订货时提出。 1.6轴承应有良好的表面多孔性。 1.7对本标准未规定的特殊技术要求应在订货时提出。 2.验收规则 2.1轴承成品应由制造厂按本标准检验合格后，并附有产品合格证方能出厂。 2.2轴承成品应按批交货验收。批量大小应在订货时注册，如不注明则由制造厂规定。 2.3有必要时订货单位可对制造厂交货的成品按批抽样检验，其方法规定如下： 2.3.1每批轴承成品任取2%，但不少于5件不多于50件，用肉眼按本标准规定检查外观质量。 2.3.2每批轴承成品任取2%，但不少于5件不多于50件，按本标准规定检查尺寸与公差。 2.3.3每批轴承成品至少任取2件样品，经脱油处理后，取得不少于50克试样，按表2的规定分析化学成分。 2.3.4每批轴承成品任取5~10件（或由双方商定），按表2规定检查物理一机械性能。 2.3.5各类抽检结果中，如有一件不合格时，仍就不合格项目抽取2倍数量的成品复 表2 注：1.铁基各类轴承的化学成分中允许有<1%的硫 2.化合碳含量允许用金相法评定。 3.铜基各类轴承化学成分中的总碳是指游离石墨。 4.在同一个试件上三点硬度值的波动范围不许超过15个不氏单位。 查，如仍有一件不合格时，则不予验收。 2.4轴承成品按以下规定方法进行检验。
最新中南大学粉末冶金原理课本重点
课程名称：粉末冶金学Powder Metallurgy Science 第一早导论 1 粉末冶金技术的发展史History of powder metallurgy 粉末冶金是采用金属粉末（或非金属粉末混合物）为原料，经成形和烧结操作制造金属材料、复合材料及其零部件的加工方法。 粉末冶金既是一项新型材料加工技术，又是一项古老的技术。 .早在五千年前就出现了粉末冶金技术雏形，古埃及人用此法制造铁器件； .1700年前，印度人采用类似方法制造了重达6.5T的“ DELI柱”（含硅Fe合金，耐蚀性好）。 .19世纪初，由于化学实验用铂（如坩埚）的需要，俄罗斯人、英国人采用粉末压制、烧结和热锻的方法制造致密铂，成为现代粉末冶金技术的基础。 .20世纪初，现代粉末冶金的发展起因于爱迪生的长寿命白炽灯丝的需要。钨灯丝的生产标志着粉末冶金技术的迅速发展。 .1923年硬质合金的出现导致机加工的革命。 .20世纪30年代铜基含油轴承的制造成功，并在汽车、纺织、航空、食品等工业部门的广泛应用。随后，铁基粉末冶金零部件的生产，发挥了粉末冶金以低的制造成本生产高性能零部件的技术优点。 .20世纪40年代，二战期间，促使人们开发研制高级的新材料（高温材料），如金属陶瓷、弥散强化合金作为飞机发动机的关键零部件。 .战后，迫使人们开发研制更高性能的新材料，如粉末高速钢、粉末超合金、高强度铁基粉末冶金零部件（热锻）。大大扩大了粉末冶金零部件及其材料的应用领域。 .粉末冶金在新材料的研制开发过程中发挥其独特的技术优势。 2粉末冶金工艺粉末冶金技术的大致工艺过程如下： 成形（模压、CIP、粉浆浇注、轧制、挤压、温压、注射成形等） 烧结（加压烧结、热压、HIP等） 粉末冶金材料或粉末冶金零部件—后续处理 Fig.1-1 Typical Process ing flowchart for Powder Metallurgy Tech nique 3粉末冶金技术的特点 .低的生产成本： 能耗小，生产率高, 材料利用率高，设备投资少。
粉末冶金技术的巨大市场潜力
粉末冶金技术的巨大市场潜力本文为大家介绍开发粉末冶金技术，促进发的核心竞争力 目前，我国汽车零部件企业不仅面临着激烈的影响的跨国企业和国内企业 激烈的同质化竞争，以及原材料成本的上游和下游的挤压和东道国经销商不断 提高标准的产品质量和我国大多数汽车零部件企业的现状是水平低的专业，产 品开发能力。绝大多数企业不具备的组成部分的产品开发，产品开发主要依和 下游的挤压和东道国经销商不断提高标准的产品质量赖于原始设备制造商，它 是难以适应的要求，车辆更换，企业核心竞争力较低自己。因此，企业在成本 上升的压力和传导不能有效的武力水平下降的企业盈利。 面对目前的困难，其核心极参与促进企业的竞争力已成为一个迫切需要解决。我们知道，汽车零件和部件的核心，高附加值是：发动机进排气门，发动 机连杆，变速箱齿轮中的同步器锥环和油泵从动齿轮，如主要的。这些地区， 主流的核心技术，粉末冶金技术。如：联系是一个重要的发动机零件，许多图 纸就引进模式提供了疲劳试验的负载连接，并呼吁在疲劳载荷周期超过5000000。和大多数国内汽车发动机杆用连杆锻造连杆和铸造中学疲劳星期超过500000是非常困难的，因为联系不属于我，酒吧的加工，小缺陷的连接更大的 影响力杆的疲劳寿命。虽然主流主要粉末锻造连杆，如：通用汽车公司别轿车，宝马德国宝马，GNK Sintermetals生产，以满足拉伸强度，甚至链接1041MPa。因此，为了培养自己的核心竞争力，这是迫切需要的动议粉末冶金技术发展计 划的一个突破在国内及零件，以提高争力已弱。 加速增长的我国汽车市场的潜力，突出粉末冶金技术市场近年来，我国汽 车产业一直保持快速发展。据中国汽车工业协会统计，2007年上半年，我国汽 车生产和销一共有4456700和4373800，增加了22.36%和23.3%。我国已成为 世界第二大汽车消费国，第三大汽车生产国，最大的潜在市场，汽车。随着大 力发展我国汽车工业，导致快速发展的零部件市场。2006，我国汽车零部件企 业销售收入达4035.00亿元。据估计，到2010年，我国国内汽车零部件生产将达到70000.0亿风格产业，导致快速发展的零部件市场。
新材料概论课程论文
新材料概论课程论文 摘要 新材料是指新近发展的或正在研发的、性能超群的一些材料，具有比传统材料更为优异的性能。新材料技术则是按照人的意志，通过物理研究、材料设计、材料加工、试验评价等一系列研究过程，创造出能满足各种需要的新型材料的技术。 一、概论 新材料（或称先进材料）是指那些新近发展或正在发展之中的具有比传统材料的性能更为优异的一类材料。新材料技术是按照人的意志，通过物理研究、材料设计、材料加工、试验评价等一系列研究过程，创造出能满足各种需要的新型材料的技术。新材料按材料的属性划分，有金属材料、无机非多属材料（如陶瓷、砷化镓半导体等）、有机高分子材料、先进复合材料四大类。按材料的使用性能性能分，有结构材料和功能材料。结构材料主要是利用材料的力学和理化性能，以满足高强度、高刚度、高硬度、耐高温、耐磨、耐蚀、抗辐照等性能要求；功能材料主要是利用材料具有的电、磁、声、光热等效应，以实现某种功能，如半导体材料、磁性材料、光敏材料、热敏材料、隐身材料和制造原子弹、氢弹的核材料等。新材料在国防建设上作用重大。例如，超纯硅、砷化镓研制成功，导致大规模和超大规模集成电路的诞生，使计算机运算速度从每秒几十万次提高到现在的每秒百亿次以上；航空发动机材料的工作温度每提高100℃，推力可增大24%；隐身材料能吸收电磁波或降低武器装备的红外辐射，使敌方探测系统难以发现，等等。 新材料技术被称为“发明之母”和“产业粮食”。 二、新材料的应用
新材料作为高新技术的基础和先导，应用范围极其广泛，它同信息技术、生物技术一起成为二十一世纪最重要和最具发展潜力的领域。同传统材料一样，新材料可以从结构组成、功能和应用领域等多种不同角度对其进行分类，不同的分类之间相互交叉和嵌套，目前，一般按应用领域和当今的研究热点把新材料分为以下的主要领域：电子信息材料、新能源材料、纳米材料、先进复合材料、先进陶瓷材料、生态环境材料、新型功能材料（含高温超导材料、磁性材料、金刚石薄膜、功能高分子材料等）、生物医用材料、高性能结构材料、智能材料、新型建筑及化工新材料等 三、新材料技术发展的方向 新材料技术的发展不仅促进了信息技术和生物技术的革命，而且对制造业、物资供应以及个人生活方式产生重大的影响。记者日前采访了中国科学院“高科技发展报告”课题组的有关专家，请他们介绍了当前世界上新材料技术的研究进展情况及发展趋势。材料技术的进步使得“芯片上的实验室”成为可能，大大促进了现代生物技术的发展。新材料技术的发展赋予材料科学新的内涵和广阔的发展空间。目前，新材料技术正朝着研制生产更小、更智能、多功能、环保型以及可定制的产品、元件等方向发展纳米材料20世纪90年代，全球逐步掀起了纳米材料研究热潮。由于纳米技术从根本上改变了材料和器件的制造方法，使得纳米材料在磁、光、电敏感性方面呈现出常规材料不具备的许多特性，在许多领域有着广阔的应用前景。专家预测，纳米材料的研究开发将是一次技术革命，进而将引起21世纪又一次产业革命。日本三井物产公司曾在去年末宣布该公司将批量生产碳纳米管，从2002年4月开始建立年产量120吨的生产设备，9月份投入试生产，这是世界上首次批量生产低价纳米产品。美国ibm公司的科研人员，在2001年4月，用碳纳米管制造出了第一批晶体管，这一利用电子的波性，而不是常规导线实现传递住处的技术突破，有可能导致更快更小的产品出现，并可能使现有的硅芯片技术逐渐被淘汰。在碳纳米管研究方兴未艾的同时，纳米事业的新秀－－“纳米带”又问世了。在美国佐治亚理工学院工作的三位中国科学家2001年初利用高温气体固相法，在世界上首次合成了半导体化物纳米带状结构。这是继发现多壁碳纳米管和合成单壁纳米管以来，一维纳米材料合成领域的又一大突破。这种纳米带的横截面是一个窄矩形结构，带宽为30～300mm，厚度为5～10nm，而长度可达几毫米，是迄今为止合成的惟一具有结构可控且无缺陷的宽带半导体准一维带状结构。
粉末冶金及模具设计 完整版
毕业设计（论文） 题目:粉末冶金及模具设计 专业:数控应用技术 班 成都电子机械高等专科学校
二〇〇七年六月 摘要 本文主要围绕粉末冶金及模具设计开展了以下几方面的研究 1、在粉末冶金技术的特点及其在新材料中的作用进行研究，重点介绍了粉末冶金在工业中的重要性及其压制步骤。 2、在粉末冶金工艺中，根据产品的要求选择金属粉末或非金属粉末为原材料来压制。 3、在粉末冶金模具设计原理方面，本文重点围绕精整模具设计进行研究，归纳、总结并提出了精整模具三个关键零部件(芯棒、模冲、阴模)。
关键词：粉末冶金粉末冶金模具精整 Abstract This text was main circumambience powder metallurgy and molding tool design to open an exhibition the following several aspect of research 1,carry on research in the new function within material in the characteristics of technique of the powder metallurgy and it,point introduction the powder metallurgy is in the industry of importance and
it inhibit a step。 2,in the powder metallurgy the craft,according to the metals powder of the request choice or nonmetal powder of product for original material to inhibit。 3,at the molding tool design of the powder metallurgy principle,this text point around Jing's whole molding tool design carry on research and induce,summary and put forward Jing the whole key with three molding tool zero partses(Xin stick,mold blunt,Yin mold)new of classification method。 Key Words:Craft and material of the powder metallurgy Powder metallurgy molding tool The Jing is whole
材料学课程论文：Al基金属玻璃的研究
本科课程论文 题目Al基金属玻璃的研究发展 院（系） 专业 课程 学生姓名 学号 指导教师 二○一二年十月
摘要：铝基非晶态合金及其非晶相复合材料均具有优异的特性,是一种具有广阔应用前景的新型结构材料。Al基非晶态合金的发展历程、玻璃形成能力、Al基金属玻璃的制备方法、研究现状、发展动向在本文中将分别介绍。 关键词：Al基金属玻璃形成能力制备展望 0 引言 自美国弗吉尼亚大学Poon研究组和日本东北大学Inoue研究组分别发现Al基合金可通过快速凝固技术形成非晶态结构[1]。Al基非晶态合金及其部分结晶后形成的纳米复合薄带材料表现出超高的比强度（5.2×105Nmkg-1）及良好的塑性，被认为是极具应用前景的新一代超高强度轻质合金。然而，与Pd、Mg、Zr、Fe等合金相比，Al基合金的玻璃形成能力较低，很难通过熔体浇铸直接形成尺度大于1mm的块体材料。Al基金属玻璃块体材料的获得主要依赖于粉末固结的途径。探索具有高玻璃形成能力、可通过熔体直接浇铸形成块体材料的合金体系始终是人们追求的目标。 1 发展历程 历史上有关非晶合金研究的最早报道 ,是在1934年 Kramer利用蒸发沉积法发现了附着在玻璃冷基底上的非晶态金属薄膜[2]。 1960 年 ,Duwez 等人采用液态金属快速冷却的方法 ,从工艺上突破了制备非晶态金属和合金的关键，引起了金属材料发展史上的一场革命[3]。 1965 年,Predecki，Giessen等人首次通过熔体急冷的方法得到铝基非晶合金(Al—Si)。 1981年 Inoue 等人开发出含铝量较高的TM(过渡金属)-Al-B 系列非晶合金[4]. 1984 年Shechman 等人在快凝Al—Mn 合金中发现具有五重对称的二十面体准晶相( Icosahedral quasicrystals phase) 。此后 ,相继在多种铝与其它过渡金属(Fe ,Cr ,Ni)的快凝合金中发现准晶相[5]。 1988 年 Y. He[6]和 A.Inoue 等人分别独立地制备了含铝量高达90%(原子分数)的轻质高强 Al- TM- Re (TM = 过渡金属 ,RE=稀土元素)非晶合金。 1990 年Inoue等人利用快凝技术得到新型的具有纳米铝晶体或纳米准晶颗粒均匀分布在非晶基体上的快凝铝基合金 ,其强度和韧性均超过了相应的铝基非晶合金。以上的发现促进了人们对铝合金的认识,引起了材料科学界的重视[7]。 近年来，沈阳材料科学国家（联合）实验室王建强研究组与美国约翰霍普金斯大学马恩教授合作。他们在Al-Tm（过渡金属）-RE（稀土）为基础的三元合金系中计算出两种分别以TM和RE作为溶质中心的原子团簇结构，通过团簇致密堆垛结构的耦合进行了合金的成分设计，在Al-Ni-Co-Y-La五元合金体系中获得了1mm直径的铝基金属玻璃棒材（铝含量达86at%）。这是国际上首次报道通过熔体直接浇铸制备出单一非晶相的铝基块体材料[8]。 2 铝基非晶合金的制备方法[9] 目前制备铝基非晶合金主要采用急冷法和机械合金化法。急冷法即快速凝固法 ,现在常用的有三种:单辊旋转快凝法、气体雾化法、表面熔化及强化法。 2.1 单辊旋转快凝法